Castable for blast furnace Iron Groove

Castable for blast furnace Iron groove
 Technical parameter

Item		Parameter
Type		Main groove		Secondary groove		Main groo-ve casta-ble	Swin-g groo-ve casta-ble	Suppor-ting iron groove castabl-e	Slag line groo-ve casta-ble	Main groo-ve casta-ble
		Iron line material	Slag line material	Iron line material	Slag line material
Model		LH-101	LH-102	LH-103	LH-104	LH-105	LH-106	LH-107	LH-108	LH-109
Chem-ical composition%	AL2O3	≥75	≥55	≥70	≥65	≥75	≥55	≥70	≥65	≥70
	SIC	≥10	≥30	≥13	≥18	≥14	≥15	≥10	≥18	≥10
Bulk density g/cm3	110°C*24h	≥3.0	≥2.9	≥2.7	≥2.6	≥3.0	≥2.9	≥2.8	≥2.8	≥2.7
	1450°C*3h	≥2.9	≥2.8	≥2.5	≥2.5	≥2.9	≥2.9	≥2.8	≥2.7	≥2.6
Strebgth of rupture(MPa)	110°C*24h	≥7.5	≥8.0	≥6.5	≥6.5	≥4.0	≥6.0	≥3.0	≥7.0	≥6.0
	1000°C*3h	≥7.0	≥7.0	≥8.0	≥7.0	≥6.0	≥8.0	≥5.5	≥6.5	≥6.0
	1450°C*3h	≥7.0	≥6.0	≥13	≥8.0	≥12.0	≥13.0	≥8.0	≥7.0	≥6.0
Strength of repture under hot stage(MPa)1450°C*3h		≥2.0	≥1.1	≥3.0	≥1.7	≥1.5	≥1.0	≥3.5	≥1.3	≥1.0
Compression strength(MPa)	110°C*24h	≥40	≥40	≥25	≥25	≥30	≥40	≥15	≥30	≥30
	1450°C*3h	≥40	≥50	≥40	≥35	≥75	≥80	≥75	≥45	≥40
Linear change rate(1450°C*2h)		-0.1	+0.03	+0.32	+0.25	+0.10	-0.10	+0.10	+0.2	+0.1
Water volume for constrution		4.5	5.0	5.5	6.0	4.5	4.5	5.0	5.0	5.2
Remark		＞2000m³ blast furnace				1000-2000m³ blast furnace			＜1000m³ blast furnace

 
Product Images




Our Company

Henan Guangda Refractories Co., Ltd is a high-tech enterprise which is dedicated to the refractory materials research and development, production, trade and engineering. Our company owns a professional technical research and development team that has been engaged in the refractory materials for decade years, owns advanced production equipments and testing equipment with the excellent marketing team. Our company has a sound management system for the market development and after-sale service. We will, as always, insist on the principle of quality first, customer first, putting quality and customers first, wholeheartedly provide the best quality......